Thermally Conductive Adhesives

Standard Products

One-Component Silicone Thermally Conductive Adhesives	TCA 01010	TCA 01510	TCA 02020	TCA 02510	TCA 03010	Test Method
Before Curing / Curing Properties
Color	White	White	Gray	White	White	Visual
Extrusion Rate (g)	35	30	32	25	20	NA
Working Time @25 °C	2H	2H	2H	2H	2H	ASTM D2240
Cure Time @25 °C	24H	24H	24H	24H	24H	ASTM D2240
Cure Time @100 °C	30min	30min	30min	30min	30min	ASTM D2240
Basic Properties After Curing
Density (g/cm³)	2.9	3.0	3.0	3.2	3.2	ASTM D792
Hardness (Shore A)	50	50	70	70	70	ASTM D2240
Shear Strength (MPa)	＞2.5	＞2.5	＞2.5	＞2.5	＞2.5	ASTM D792
Operating Temperature Range (°C)	-50~+150	-50~+150	-50~+150	-50~+150	-50~+150	NA
Thermal / Electrical / Flame Retardancy
Thermal Conductivity (W/m·K)	1.0	1.5	2.0	2.5	3.0	ASTM D5470
Dielectric Strength	＞10	＞10	＞10	＞10	＞10	ASTM D149
Volume Resistivity	＞1.0×10¹³	＞1.0×10¹³	＞1.0×10¹³	＞1.0×10¹³	＞1.0×10¹³	ASTM D150
Relative Permittivity	＞5	＞5	＞5	＞5	＞5	ASTM D257
Flame Rating	V-0	V-0	V-0	V-0	V-0	UL 94

Two-Component Silicone Thermally Conductive Adhesives	TSA 01010	TSA 01510	TSA 02010	TSA 02510	TSA 03010	Test Method
Basic Properties Before Curing
Color	White	White	Gray	White	White	Visual
Mixed Viscosity (mPa·s)	5,000	6,500	9,500	12,000	15,000	ASTM D2196
Curing Properties
Mix Ratio	1:1	1:1	1:1	1:1	1:1	NA
Working Time @25 °C	2H	2H	2H	2H	2H	ASTM D2240
Cure Time @25 °C	24H	24H	24H	24H	24H	ASTM D2240
Cure Time @100 °C	30min	30min	30min	30min	30min	ASTM D2240
Basic Properties After Curing
Density (g/cm³)						ASTM D792
Hardness (Shore 00)	50	50	60	70	90	ASTM D2240
Shear Strength (MPa)	＞2.5	＞2.5	＞2.5	＞2.5	＞2.5	ASTM D792
Operating Temperature Range (°C)	-50~+150	-50~+150	-50~+150	-50~+150	-50~+150	NA
Thermal Properties
Thermal Conductivity (W/m·K)	1.0	1.5	2.0	2.5	3.0	ASTM D5470
Electrical Properties / Flame Retardancy
Dielectric Strength	＞10	＞10	＞10	＞10	＞10	ASTM D149
Volume Resistivity	＞1.0×10¹³	＞1.0×10¹³	＞1.0×10¹³	＞1.0×10¹³	＞1.0×10¹³	ASTM D150
Relative Permittivity	＞5	＞5	＞5	＞5	＞5	ASTM D257
Flame Rating	V-0	V-0	V-0	V-0	V-0	UL 94

Custom Development

TCA 03510HP

Efficient thermal conduction that lowers temperature rise and keeps equipment running reliably
Strong bonding that simplifies structures and reduces weight
Low volatility, with very few by-products during curing, greatly reducing the risk of contaminating precision circuits

Color	White
Thermal Conductivity (W/m·K)	3.5
Viscosity (cps)	100,000
Recommended Operating Temperature (°C)	-50~+175
Flame Rating	V-0

TCA and TSA Series Silicone Thermally Conductive Adhesives